LCP 美国杜邦 6140L WT010
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 比重 | ASTM D-792 | 1.71 | ||
| 机械性能 | 拉伸强度 | 3.2mm | ASTM D-638 | 135 | MPa |
| IZOD冲击强度 | 3.2mm | ASTM D-256 | 80 | J/m | |
| 弯曲模量 | 3.2mm | ASTM D-790 | 15600 | MPa | |
| 断裂伸长率 | 3.2mm | ASTM D-638 | 1.3 | % | |
| 弯曲强度 | 3.2mm | ASTM D-790 | 182 | MPa | |
| 热性能 | RTI,Mechanical with Impact | 0.8mm | UL 746-B | 130 | ℃ |
| 玻璃化转变温度 | ASTM D-3418 | 120 | ℃ | ||
| 熔点 | ASTM D-3418 | 335 | ℃ | ||
| RTI,Mechanical with Impact | 1.5mm | UL 746-B | 210 | ℃ | |
| 热变形温度 | 1.80MPa | ASTM D-648 | 271 | ℃ | |
| 解链温度范围 | 350-360 | ℃ | |||
| RTI,Mechanical with Impact | 3.0MPa | UL 746-B | 220 | ℃ | |
| RTI,Mechanical without Impact | 0.8mm | UL 746-B | 240 | ℃ | |
| 模压温度范围 | 30-95 | ℃ | |||
| RTI,Electrical | 0.8mm | UL 746-B | 240 | ℃ | |
| 干燥温度 | 135 | ℃ | |||
| RTI,Mechanical without Impact | 1.5mm | UL 746-B | 240 | ℃ | |
| RTI,Mechanical without Impact | 3.0mm | UL 746-B | 240 | ℃ | |
| RTI,Electrical | 3.0mm | UL 746-B | 240 | ℃ | |
| RTI,Electrical | 1.5mm | UL 746-B | 240 | ℃ | |
| 其它性能 | Thickness Tested | UL 94 | 0.75 | mm | |
| 工业含水量 | <0.01 | % | |||
| Rating@Thickness | UL 94 | V-0 | |||