PC 广州LG SC-1004耐候pc
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
| 物理性能 | 比重 | ASTM D792 | 1.25 | |||
| 成型收缩率 | ASTM D955 | 0.2-0.4 | % | |||
| 机械性能 | 拉伸强度 | - | ASTM D638 | 740 | kg/cm2 | |
| - | ASTM D638 | 73 | MPa | |||
| - | ASTM D638 | 10500 | psi | |||
| 断裂伸长率 | ASTM D638 | 10 | % | |||
| 弯曲强度 | - | ASTM D790 | 1300 | kg/cm2 | ||
| - | ASTM D790 | 130 | MPa | |||
| - | ASTM D790 | 18500 | psi | |||
| 弯曲模量 | - | ASTM D790 | 37000 | kg/cm2 | ||
| - | ASTM D790 | 3625 | MPa | |||
| - | ASTM D790 | 525 | psi | |||
| Izod缺口冲击强度 | - | 23℃ | ASTM D256 | 10 | Kg.cm/cm | |
| - | 23℃ | ASTM D256 | 98 | J/m | ||
| - | 23℃ | ASTM D256 | 1.8 | ft.ib/in | ||
| 洛氏硬度 | ASTM D785 | 124 | R | |||
| 热性能 | 热变形温度 | - | 1.82MPa | ASTM D648 | 142 | ℃ |
| - | 1.82MPa | ASTM D648 | 290 | ℉ | ||
| 阻燃性 | 1.5mm | UL94 | V-0 | |||
展开全文